WANG Chunting, YE Yuwei, HU Jianmin, CHEN Hao, WANG Yongxin, LI Jinlong. Tribological performances of CrCN coatings under different deposition temperatures[J]. Nonferrous Metals Science and Engineering, 2015, 6(2): 42-47. DOI: 10.13264/j.cnki.ysjskx.2015.02.008
Citation: WANG Chunting, YE Yuwei, HU Jianmin, CHEN Hao, WANG Yongxin, LI Jinlong. Tribological performances of CrCN coatings under different deposition temperatures[J]. Nonferrous Metals Science and Engineering, 2015, 6(2): 42-47. DOI: 10.13264/j.cnki.ysjskx.2015.02.008

Tribological performances of CrCN coatings under different deposition temperatures

More Information
  • Received Date: January 17, 2015
  • Published Date: April 29, 2015
  • CrCN coatings with different deposition temperatures (150℃、250℃、350℃、450℃) are deposited on 316L stainless steel and single crystal silicon by Multi -Arcion plating technique. Microstructures, mechanical performance and tribological performances in ambient air and water are systematically investigated by XRD, XPS, SEM, nano-indentation and ball-on-disc tribol-meter. The results show that the hardness and modulus increase with the increasing of deposition temperature and reach theclimax with deposition temperature at 450 ℃ and the maximum value at about 24 Gpa and 354 Gpa, respectively. Both the friction coefficients and wear rates of CrCNcoatings in ambient air and water tent to decrease after increasing first and reach the bottom with deposition temperature at 350 ℃. The friction coefficient in ambient airand water are about 0.38 and 0.23, the maximum value of wear rate in ambient air and water are about 1.717 1×10-6mm3/N▪m and 9.529 7×10-7mm3/N▪m, respectively. Meanwhile, the friction coefficients and wear rates of CrCN coatings in water are lower than that in ambient air, which is attributed to the good lubrication of waterduring the friction.
  • [1]
    Meicke S,Paasch R,Seawater lubricated polymer journal bearings for use in wave energy converters[J]. Renewable Energy,2012,39: 463-470.
    [2]
    Wang Q,Zhou F,Wang X,et al. Comparison of tribological prop­erties of CrN,TiCN and TiAlN coatings sliding against SiC balls in water[J]. Applied Surface Science,2011,257: 7813-7820. doi: 10.1016/j.apsusc.2011.04.035
    [3]
    Wang C T,Gao N,Gee Mark G,et al. Processing of an ultrafine­grained titanium by high -pressure torsion: An evaluation of the wear properties with and without a TiN coating[J]. Journal of Me­chanical Behavior of Biomedical Material,2013,17 : 166-175. doi: 10.1016/j.jmbbm.2012.08.018
    [4]
    Deng B,Tao Y,Guo D L. Effects of vanadium ion implantation on microstructure, mechanical and tribological properties of TiN coatings[J]. Applied Surface Science,2012,258(22): 9080-9086. doi: 10.1016/j.apsusc.2012.06.001
    [5]
    Ono T,Uemurn M,Yatsuzuka M. Adhesion improvement of TiN film on tool steel by a hybrid process of unbalanced magnetron sputtering and plasma-based ion implantation[J]. Nuclear Instru­ments and Methods in Physics Research Section B: Beam Inter­actions with Material and Atoms,2007,257(1/2): 786-789. http://cn.bing.com/academic/profile?id=1986961228&encoded=0&v=paper_preview&mkt=zh-cn
    [6]
    李国亮,肖厚群,揭晓华,等.液相脉冲放电制备TiCN多元陶瓷涂 层[J].中国表面工程,2013, 262(2): 82-86. http://www.cnki.com.cn/Article/CJFDTOTAL-BMGC201302022.htm
    [7]
    古柏林,刘捍卫,朱旻昊,等.TiN/Ti复合涂层高温微动磨损特性 研究[J].中国表面工程,2010, 23(3): 89-94. http://www.cnki.com.cn/Article/CJFDTOTAL-BMGC201003024.htm
    [8]
    龚才,代明江,陈明安,等.基体材料对TiN薄膜表面液滴及薄膜结合力的影响[J].中国表面工程,2013, 26(1): 27-33. http://www.cnki.com.cn/Article/CJFDTOTAL-BMGC201301008.htm
    [9]
    付英英,李红轩,吉利,等.CrN和C.A1N薄膜的微观结构及在不同 介质中的摩擦学性能[J].中国表面工程,2012, 25(6): 34-41. http://www.cnki.com.cn/Article/CJFDTOTAL-BMGC201206009.htm
    [10]
    叶育伟,陈颢,王永欣,等.316L不锈钢表面沉积C.C/薄膜的 结构及性能研究[J].有色金属科学与工程,2014, 5(4): 49-54.
    [11]
    叶育伟,陈颢,王永欣,等.不同过渡层对C.C/涂层性能影响[J]. 有色金属科学与工程,2014,5(6):61-66.
    [12]
    Wang Q Z,Zhou F,Ding X D,et al. Microstructure and water- lubricated friction and wear properties of CrN (C) coatings with different carbon contents[J]. Applied Surface Science,2013,268: 579-587. doi: 10.1016/j.apsusc.2013.01.027
    [13]
    Warcholinski B, Gilewicz A. Effect of substrate bias voltage on the properties of CrCN and CrN coatings deposited by cathodic arc evaporation[J]. Vacuum,2013,90: 145-150. doi: 10.1016/j.vacuum.2012.04.039
    [14]
    Hu P F,Jiang B. Study on tribological property of CrCN coating based on magnetron sputtering plating technique[J]. Vacuum,2011,85: 994-998. doi: 10.1016/j.vacuum.2011.02.007
    [15]
    Zhang S,Bui X L,Fu Y.Megnetron sputtered hard a-C coatings of very high toughness[J]. Surface and Coatings Technology,2003, 167: 137-142. doi: 10.1016/S0257-8972(02)00900-3
    [16]
    Choo J H,Spikes H A,Ratoi M,et al. Friction reduction in low- load hydrodynamic lubrication with a hydrophobic surface[J]. Tri­bology International, 2007, 40: 154-159. doi: 10.1016/j.triboint.2005.09.006
    [17]
    Polcar T,Vitu T,Cvrcek L,et al. Effects of carbon content on the high temperature friction and wear of chromium carbonitride coatings[J]. Tribology International,2010,43: 1228-1233. doi: 10.1016/j.triboint.2009.12.010
    [18]
    Zhang H S,Endrino J L,Anders A. Comparative surface and nano-tribological characteristics of nanocomposite diamond-like carbon thin films doped by silver[J|. Applied Surface Science,2008, 255: 2551-2556. doi: 10.1016/j.apsusc.2008.07.193
    [19]
    胡树兵,李志章,催崑.过渡层对TiN涂层结合力的影响[J].材料保护,2001,34(9): 1-3.
  • Related Articles

    [1]ZHANG Qinying, CHEN Hao, REN Xingrun, WEN Yan. Effect of Al target sputtering power on themicrostructure and tribological properties of CrAlN coatings[J]. Nonferrous Metals Science and Engineering, 2017, 8(5): 109-114. DOI: 10.13264/j.cnki.ysjskx.2017.05.016
    [2]LIU Wenyang, ZHANG Jianbo, WU Shanjiang, HU Meijun, CHEN Tingting, GUO Lili. Effects of Si on friction properties of Ti3SiC2/Al composites[J]. Nonferrous Metals Science and Engineering, 2017, 8(5): 89-94. DOI: 0.13264/j.cnki.ysjskx.2017.05.013
    [3]LIU Meixia, HUANG Zhu, LI Tianbai, REN Xingrun, ZHANG Xuehui, CHEN Hao. Effect of Al2O3 concentration on properties of Ni-W-Al2O3 composite coatings[J]. Nonferrous Metals Science and Engineering, 2016, 7(4): 55-60. DOI: 10.13264/j.cnki.ysjskx.2016.04.010
    [4]ZHANG Xuehui, ZHANG Biao, ZHU Taiheng, WANG Cheng, YU Yinhong, CHEN Hao. Frictional wear behavior of tungsten heavy alloys 93W-4.9Ni-2.1Fe[J]. Nonferrous Metals Science and Engineering, 2016, 7(4): 33-39. DOI: 10.13264/j.cnki.ysjskx.2016.04.006
    [5]HUANG Zhu, LIU Meixia, LI Tianbai, ZHANG Xuehui, CHEN Hao. Friction and wear properties of electro-deposited Ni-W-WC composite coatings[J]. Nonferrous Metals Science and Engineering, 2016, 7(3): 66-70. DOI: 10.13264/j.cnki.ysjskx.2016.03.012
    [6]Liu Long, Zhou Shengguo, Wang Yuechen, Liu ZhengBing, Ma LiQiu. Microstructures and tribological properties of a-C:H film prepared by DC reactive magnetron sputtering[J]. Nonferrous Metals Science and Engineering, 2016, 7(1): 41-47. DOI: 10.13264/j.cnki.ysjskx.2016.01.009
    [7]DU Ping, WU Bo, CHEN Junwei, LI Zhihua, XU Hongyan, XU Bingsheng, ZHANG Lina, YUAN Zhangfu. Application of spray technology of wear resistant coating in CDQ furnace[J]. Nonferrous Metals Science and Engineering, 2015, 6(2): 1-6. DOI: 10.13264/j.cnki.ysjskx.2015.02.001
    [8]YE Yuwei, CHEN Hao, WANG Yongxin, LI Jinlong. Effects of different interlayers on CrCN coatings properties[J]. Nonferrous Metals Science and Engineering, 2014, 5(6): 61-66. DOI: 10.13264/j.cnki.ysjskx.2014.06.010
    [9]WANG Meng, ZHU Zhi-yun, FENG Yan, WEI Xiao-feng. Tribological properties of Ni-Cr/hBN self-lubricating composite[J]. Nonferrous Metals Science and Engineering, 2013, 4(6): 37-42. DOI: 10.13264/j.cnki.ysjskx.2013.06.009
    [10]WU Yong-sheng. Causes analyzed and takened countermeasure to the gold displacement rate's decrease[J]. Nonferrous Metals Science and Engineering, 2011, 2(5): 36-40.
  • Cited by

    Periodical cited type(8)

    1. 齐白羽,王丁,王卓,卢昌祥,刘静静. 低温乙醇分离-电感耦合等离子体原子发射光谱法测定粗铅中金. 理化检验(化学分册). 2021(11): 977-980 .
    2. 张俊峰,栾海光,王飞虎. 直接灰吹﹣ICP-AES测定粗铅中的金、银、铂和钯. 贵金属. 2021(04): 66-70 .
    3. 陈永红,孟宪伟,刘正红,王立臣. 2017—2018年中国金分析测定的进展. 黄金. 2020(01): 82-90 .
    4. 陈永红,洪博,孟宪伟,芦新根. 2017—2018年中国银分析测定的进展. 黄金. 2020(02): 81-86 .
    5. 王景凤. 电感耦合等离子体原子发射光谱法测定镍矿石中的铂和钯. 化学分析计量. 2019(01): 76-80 .
    6. 王丽,马会春,庞雪敏,张兆法,武静,赵良成. 活性炭动态吸附ICP-AES法测定粗铅中的金. 中国测试. 2019(04): 58-62 .
    7. 龙海珍,王景凤,王茂盛,孔会民. 火试金富集—重量法测定锌阳极泥中银含量的方法. 有色金属科学与工程. 2019(06): 76-80 . 本站查看
    8. 王景凤,张瑾,董哲飞. 青海某高硅复杂金矿石中金银含量测定方法研究. 有色金属科学与工程. 2018(06): 89-93 . 本站查看

    Other cited types(0)

Catalog

    Article Metrics

    Article views (75) PDF downloads (3) Cited by(8)
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return